Effects of low-temperature pretreatment on carbonization of cellulose for the production of biocarbons

Abstract

Pretreatment of cellulose at temperatures below 300 °C prior to carbonization at 1200 °C was studied for the production of high-yield biocarbons. Filter paper as the cellulosic raw material was pyrolyzed by using heating schemes, including 16-h isothermal step at 215–270 °C under nitrogen atmosphere, followed by fast heating up to 600 °C and finally to 1200 °C. Cellulose degradation was completed in the 16-h holding isothermal step at a temperature above 250 °C, as confirmed by IR spectroscopy and X-ray diffraction. The yield of char was increased from 11% to 21% by pretreatment of cellulose after post-treatment at 600 °C or 1200 °C. The BET surface area as the microporosity value was also significantly enhanced from 461 m2/g to 837 m2/g by straight heating of 10 °C/min. These results are thought to be caused by slow heating and stabilizing effects due to pretreatment of cellulose at the critical temperature for degradation.