Abstract
This work reports the effects of low-temperature post-deposition annealing (PDA) and post-metallization annealing (PMA) on the electrical properties of ultrathin (with EOT ranging from 1.29 nm to 2.33 nm) La2O3 gate dielectric films. We found that positive charges were generated during the PDA as evidenced by the negative flat-band voltage (VFB) shift. Forming of La-silicate interface layer and a reduction in the channel mobility are found for the PDA samples at temperature higher than 300°C. Better electrical characteristics were achieved by the PMA. The PMA sample has a peak channel mobility of 319 cm2 /Vs.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callSimilar Papers
More From: Microelectronic Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.