Abstract
The influence of temperature in the range of 24 to 260 °C and load ratio on the near-threshold fatigue crack growth rate behavior of a CrMoV steel was characterized. At all temperatures investigated, the threshold stress intensity range, ΔKth, for fatigue crack growth decreased with increasing load ratio. The near-threshold crack growth rates increased significantly at 149 °C when compared with the rates at room temperature. However, the crack growth rates at 260 °C were comparable to those at 149 °C. These observations are rationalized in terms of the concepts of roughness and oxide-induced crack closure. Extensive fracture surface characterization using SEM, oxide thickness measurements by Auger spectroscopy, and roughness measurements by light-section-microscopy were conducted to substantiate the explanations.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.