Abstract
A laser shock peening (LSP) treatment was performed on AA7075-T651 for maximum fatigue improvement. Surface and microstructural characterisation techniques (micro-hardness, SEM-EBSD, contact-profilometry) showed LSP surface modification was limited, and LSP generated deep compressive residual stresses above −300 MPa. Fatigue testing showed a two-order magnitude increase in overall life, due to the mechanism of crack initiation changing from surface second-phase particles to subsurface crack initiation dependent on the local stress field. Modelling highlights the sensitive balance between surface roughness (including LSP-induced pits) and residual stress on the micro-mechanism of crack initiation, and how this can be used to maximise fatigue life extension.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.