Abstract
HfC, TaC and SiC with different proportions were introduced into Cf/LaB6 preform to fabricate four kinds of UHTC doped C/C composites. Results show that LaB6 could react with HfC or TaC to establish a compact ceramic structure. After ablation for 120 s, the composites doped with LaB6-HfC-TaC-SiC possessed the best ablation property, and the ablation rates were 1.129 mg/s and 3.133 μm/s. A layer with La2Si2O7, La2Hf2O7 and LaTaO4 is observed due to the reactions between La2O3 and other binary oxides. Further ablation was suppressed and stability of the multi-phase layer is therefore confirmed, indicating good coordination among the oxides.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.