Abstract
Film fabrication of LiTaO3 has been successfully prepared with 0%, 2%, 4%, and 6% Iron containing variations using the Chemical Solution Deposition (CSD) method. Each sample was characterized using FTIR and the wavenumber and transmittance values were obtained. This value was analyzed using the Kramers-Kronig (KK) method and obtained the Transverse Optic (TO) and Longitudinal Optic (LO) values. The results show that TO value is in wave numbers 462.25 cm-1 – 556.00 cm-1. While the value of LO is in the range of wave numbers 478.50 cm-1 – 571,00 cm-1. The results show an increase in both TO and LO values as the Iron Oxide percentage increases. Based on the analyses of TO, LO, ε₁ and ε₂, film fabrication of LiTaO3 has the potential as light, pressure and temperature sensors.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Nanoelectronics and Materials (IJNeaM)
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.