Abstract
Prealloyed p and n-type bismuth telluride-based materials produced by bulk mechanical alloying are directly one-step hot-pressed to yield a thermoelectric pn junction. Variation of constitutional element concentrations across the pn interface is characterized by EPMA to determine the interface thickness of the pn junction. The electrical resistivity of the interface layer is greater than that of both p and n semiconductor materials. Analytic expressions for Seebeck coefficient and figure of merit versus interface layer size are deduced. The Seebeck coefficient of the pn junction is inversely proportional to the ratio of the interface layer length to the pn junction height ( h i/ h) and agrees well with experimental results. In a pn junction with an interface layer certain thickness, there is a maximum figure of merit at the optimal h i/ h; with the decrease in interface thickness, the maximum increases, and correspondingly, the optimal h i/ h decreases. In other words, the pn composite billet with a thinner interface layer can attain a larger figure of merit at the same h i/ h than that with a thicker interface. Adjusting the process parameter, with proper cutting, thermoelectric properties can be improved greatly; this method of producing a pn junction is feasible.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.