Abstract
Four heats of commercially available JIS SNCM439 steel are prepared, and fatigue tests are conducted in air and hydrogen gas. The materials evaluated are all martensitic steel with a tensile strength of 900 MPa or less and contain nonmetallic inclusions of different sizes. A decrease in the fatigue limit is observed in the specimens with large nonmetallic inclusions, but the fatigue limit in air is approximately equal to the fatigue strength at 300,000 cycles in hydrogen. However, in the finite life region, the fatigue life in hydrogen significantly decreases owing to the presence of large nonmetallic inclusions. It was observed that hydrogen considerably affects the fatigue life even at low stress amplitudes close to the fatigue limit. This effect is considered to be dependent on the size of the initial crack originating from the nonmetallic inclusions; large nonmetallic inclusions accelerate the hydrogen-induced fatigue crack growth rate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.