Abstract
AbstractThe fracture response of injection molded short glass fiber (GF) reinforced and rubber‐toughened poly(butylene terephthalate) (PBT) composites has been characterized by the fracture toughness (Kc) and energy (Gc), measured on static‐loaded compact tension (CT) specimens. The related failure of the composites with 30 wt% GF reinforcement in as‐received (AR), hygrothermally aged (HA) and re‐dried (RD) states, respectively, was studied by acoustic emission (AE) and fractography. Tougheners were functionalized ethylene/acrylate (EAF), crosslinked acrylate (XAR) and core‐shell type (CSR) rubbers, at 20 wt% in the composites. It was shown that both Kc and Gc decrease with hygrothermal aging at 90°C, and their values cannot be restored by subsequent drying. This is attributed to severe hydrolysis degradation of the PBT matrix. Deterioration in the fracture parameters was affected by the composition of the rubbery toughener: The toughness retention by EAF was superior to the other modifiers. The difference in the failure mode of the GF‐PBT composites before and after hygrothermal aging was revealed by viewing the fracture surface of the CT‐specimens in scanning electron microscope (SEM). Based on the fractographic results, changes in the AE amplitude envelopes are interpreted and discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.