Abstract
The effects of hydrogen on the tensile properties and fracture surface morphologies of Type 316L stainless steel were investigated using virgin and prestrained specimens. Hydrogen gas exposure at 10 MPa and 250 °C for 192 h resulted in its uniform distribution in the specimens. Such internal hydrogen degraded the tensile ductility of the specimens. Cup–cone fracture occurred in the non-, Ar-, and H-exposed specimens. The fracture surfaces were covered with large and small dimples. The H-exposed specimens exhibited larger small-dimple areas than the non- and Ar-exposed ones. The diameter of the large dimples decreased with increasing small-dimple area. Three-dimensional analysis of the dimples showed that the small-dimple regions were void sheets produced by local shear strain. Hydrogen accelerated nucleation of voids and formation of the void sheets by enhancing localization of shear deformation, thereby reducing the average size of the dimples.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.