Abstract
The uni-axially aligned ZnO nanofibers with diameters of ∼200 nm were prepared by electrospinning followed by calcination at 600 °C. The effects of humidity and UV illumination on the electrical properties of electrospun ZnO nanofibers were investigated in air under different levels of relative humidity (RH). In the air with low RH, the photocurrent of the electrospun ZnO nanofiber based device increased approximately three orders of magnitude under UV illumination compared with the value measured in the dark. Intriguingly, the photocurrent increased in the air with increase of RH initially; when the RH was above ∼50%, the photocurrent decreased gradually. In the recovery step when the UV illumination was off, a faster current decay was observed with the increase of RH. These were attributed to the competitive surface effects resulted from adsorption/desorption and the related ionization/dissociation of oxygen and water molecules on the photo-generated charge carriers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.