Effects of hot rolled microstructure after twin-roll casting on microstructure, texture and magnetic properties of low silicon non-oriented electrical steel

Abstract

In this work, a 0.71wt%Si+0.44wt%Al as-cast strip was produced by novel twin-roll casting. Some as-cast samples were respectively reheated and hot rolled at different temperatures in order to obtain different microstructure prior to cold rolling and annealing. The effects of the hot rolled microstructure on microstructure, texture evolution and magnetic properties were investigated in detail. A coarse deformed microstructure with λ-fiber texture was formed after hot rolling at 850–1050°C, finally leading to an inhomogeneous recrystallization microstructure with strong λ-fiber, Goss and extremely weak γ-fiber texture. By contrast, a fine transformed microstructure was formed after hot rolling at 1150–1250°C, finally leading to a fine and homogeneous recrystallization microstructure with stronger α-fiber, γ-fiber and much weaker λ-fiber texture. It should be noted that both the magnetic induction and core loss non-monotonically decreased or increased according to the hot rolling temperature. The unfavorable α-fiber and γ-fiber textures in the annealed sheets were much weaker than those of the conventional products regardless of the hot rolling temperature, thus contributing to a much higher magnetic induction. However, the average grain size in the annealed sheets was much lower than those of the conventional products regardless of the hot rolling temperature, thus leading to a higher core loss except the case of 1050°C. Hence, it is underscored that better integrated magnetic properties than those of the conventional products can be obtained by optimizing the hot rolled microstructure to produce final desirable recrystallization microstructure and texture.