Abstract
AA8021 aluminum alloy twin-roll cast strips with 7mm gauge were rolled to 3.8mm gauge sheets and given homogenization, further rolled into 0.55mm gauge foil stocks with intermediate annealing. This paper investigated the influence of homogenization conditions on microstructures of foil stocks in detail. The results show that, for the foil stock made from the sheet without homogenization, the grain structure is partially recrystallized. While the grain structure of foil stock made from the sheet with medium temperature homogenization is fully recrystallized, but it is coarse near sheet surface. However, foil stock made from the sheet with high temperature homogenization has fine and uniform recrystallized grain structures. The differences of grain structures among these three kinds of foil stocks can be understood by the variation in solid solution content of Fe, Si, Mn and distribution of intermetallic compounds. The optimized homogenization condition was adopted by our plant to produce foil stock, and its grain structure was fine and uniform. The surface quality of final aluminum foil rolled from the foil stock could meet high grade requirements of customers.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.