Abstract
The feasibility of fabricating ZA84 magnesium alloy with non-dendritic microstructure by a semi-solid isothermal heat treatment process and the effects of holding temperature and time on the semi-solid isothermal heat-treated microstructure of the alloy were investigated. The results indicate that it is possible to produce ZA84 alloy with non-dendritic microstructure by suitable semi-solid isothermal heat treatment. After being treated at 560-575 °C for 120 min, ZA84 magnesium alloy can obtain a non-dendritic microstructure with 14.2%-25.6% liquid fraction and an average size of 56-65 μm of the unmelted primary solid particles. With the increasing holding time from 30 to 120 min or holding temperature from 560 to 575 °C, the average size of unmelted primary solid particles decreases and globular tendency becomes more obvious. Under the experimental condition, the microstructural evolution of ZA84 alloy during semi-solid isothermal treatment is mainly composed of three stages of initial coarsening, structural separation and spheroidization. The subsequent coarsening of spheroidal grains is not observed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.