Abstract
In this paper, TiB reinforced Ti-6Al-4V matrix composites were successfully fabricated using a spark plasma sintering, hot rolling and heat treating process. (Transformed β-Ti + secondary α-Ti) domains were formed in TiB/TMCs after heat treatment. The size of these domains increases from 2.5 μm to 4.6 μm with the increase of solution time. The aspect ratio of whiskers monotonously decreases along with the solution time extending. The highest ultimate tensile strength of 1332 MPa and yield-strength of 1315 MPa were achieved by (940 °C, 15min+ water-quenching+537 °C, 4h) TMC.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.