Abstract
In this study, the mechanical properties of butt-welded thin plates made of S700, S960 and S1100 steels under various heat inputs (HI) are investigated. The gas metal arc welding (GMAW) process with two different levels of HI, and laser welding (LW) are implemented for this purpose. Fully automated welding process is employed to attain high quality and homogeneous weldments. Standard tensile tests of the butt-welded joints, together with micro-hardness measurements are conducted in this study. The microstructure of the heat affected zones (HAZ) of the weldments are closely examined using scanning electron microscopy (SEM). It was observed that while the fracture was occurred at the base materials of all S700 and S1100 weldments, the S960 suffered from failure at the HAZ which resulted in reduction of the joint’s strength and ductility. For all the studied steels, it was found that the joint’s ductility is highly dependent on HI values over the range of 0.3–1.4 kJ/mm for each welding pass. Though, the S1100 steel showed the best performance under welding HI with a moderate change in its mechanical properties and a stable microstructure after welding compared to S700 and S960.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.