Abstract
Al-doped zinc oxide (AZO) thin films have been grown on (0001) substrate by radio-frequency (rf) magnetron sputtering at 550°C. The AZO films have been annealed by a rapid thermal process in exposure with a temperature range of 600-1000°C. Effects of hydrogen on the AZO films have been investigated using photoluminescence (PL), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM). The as-grown AZO film shows only broad deep defect-level PL. After annealing at 600°C, deep defect-level emission is quenched and near-band-edge (NBE) emission is observed at around 382 nm (3.2 eV), which can be explained by the passivation effect. At elevated temperature, two interesting peaks corresponding to violet (406 nm, 3.05 eV) and blue (436 nm, 2.84 eV) emissions have been observed for the first time in annealed AZO thin films. Incorporation of hydrogen and formation of oxygen deficient in annealed AZO films have been studied using XPS. Surface morphology and microstructure of AZO films have been carried out by SEM. © 2003 The Electrochemical Society. All rights reserved.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.