Abstract
The effect of grain boundary character distribution (GBCD) on hydrogen-induced cracks (HICs) initiation and propagation in nickel-saving austenitic stainless steel was investigated at different strain rates with electrochemical hydrogen charging. The fracture strength and elongation of specimens decreased as the strain rates decreased due to more hydrogen atoms being transported by mobile dislocations. HICs are more likely to initiate at random grain boundaries (RGBs) because of poor deformation coordination of adjacent grains at RGBs after hydrogen charging. Special boundaries (SBs) deflected HICs and hindered the propagation of HICs owing to a more stable boundary structure and less strain localization during slow strain rate tensile (SSRT) deformation with hydrogen charging. Furthermore, highly efficient distributions of SBs contribute to great resistance to hydrogen embrittlement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.