Abstract
The effects of Bi2O3 addition on the microwave dielectric properties and the microstructures of Zn0.95Mg0.05TiO3 + 0.25TiO2 with 1 wt% 3ZnO–B2O3 (ZnBO–ZMT') ceramics prepared by conventional solid-state routes have been investigated. In a preliminary study, it was shown that ZnBO–ZMT' ceramics can be sintered to a theoretical density higher than 95% at 900°C. In this study, the effects of Bi2O3 additions of up to 10 wt% on the sintering characteristics of the ZnBO–ZMT' ceramics was investigated at the sintering temperatures ranging from 860 to 960°C. Sintered ceramic samples were characterized by X-ray diffraction and scanning electron microscopy (SEM). It was found that as the content of Bi2O3 increases, the density of the sintered ceramics increases, and the sintering temperature can be lowered to 880°C by adding 5 wt% Bi2O3. The ZnBO–ZMT' ceramic with 5 wt% Bi2O3 addition sintered at 880°C exhibits the optimum dielectric properties: Q×f=4000 GHz, εr=24.6, and τf=-14 ppm/°C. Unlike the ZnBO–ZMT' ceramic without Bi2O3 addition sintered at above 920°C, the ceramics with Bi2O3 additions show no Zn2TiO4 existence at 960°C sintering. It is therefore demonstrated that the addition of Bi2O3 can suppress the formation of Zn2TiO4 in ZnBO–ZMT' ceramics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.