Effects of Gate Dielectric and Process Treatments on the Electrical Characteristics of IGZO TFTs With Film Profile Engineering

Abstract

In this paper, high-performance InGaZnO (IGZO) thin-film transistors were fabricated with film-profile-engineering scheme. The impacts of gate dielectric, O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> /Ar ratio during the sputtering of the IGZO, and annealing ambient on the device performance were investigated. It is found that the turn-ON voltage of the device is closely related to the gate dielectric material. For the devices with Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> as the gate dielectric, decent performance in terms of high ON/OFF current ratio (>10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">8</sup> ), extremely steep subthreshold swing (62 mV/decade), and good mobility (19.8 cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> /V·s) is obtained. The influences of O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> /Ar flow ratio are distinct for the devices with Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> gate oxide. Significant improvement in the stability of the devices to the environment is achieved with the anneal done in a low-pressure N <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> ambient.