Abstract
Crystalline solutions of 0.65 Bi(0.94)La(0.06)) (Ga(x)Fe(1-x))O(3)-0.35PbTiO(3) Ceramics (BLGF-PT) for x = 0 and 0.05 have been fabricated by the solid-state reaction method. X-ray diffraction (XRD) was utilized to characterize the crystal structure and examine any possible impurities existing in the ceramics. The effects of Ga substitution on dielectric properties of the samples were studied at frequencies from 10(2) to 10(6) Hz over a temperature range from 20 to 620 degrees C. The results indicate that Ga modification can reduce the room temperature dielectric loss. The conduction mechanism of the material was investigated using ac conductivity. It is concluded that electrons originating from Fe(2+) and oxygen ion vacancies are the main charge carriers, and Ga doping could decrease the electronic conduction effectively. The frequency dependence of ac conductivity was found to follow Jonscher's universal power law.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IEEE Transactions on Ultrasonics, Ferroelectrics and Frequency Control
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.