Abstract
In this study, ASTM A529 carbon–manganese steel angle specimens were joined by flash butt welding and the effects of varying process parameter settings were investigated. The resulting weld metal and heat affected zones were examined and further processed using tensile testing, Rockwell hardness testing, ultrasonic scanning, optical microscopy, and scanning electron microscopy with energy dispersive spectroscopy. Test results showed that hardness was increased in the weld zone for all specimens, which can be attributed to the extensive deformation of the upset operation. Statistical analysis of experimental data highlighted the sensitivity of weld strength and the presence of weld zone inclusions and interfacial defects to the process factors of upset current, flashing time duration, and upset dimension. Microstructural analysis revealed various phases within the weld and heat affected zone, including acicular ferrite, Widmanstatten or side-plate ferrite, and grain boundary ferrite. Fractography of tensile specimens indicated brittle cleavage fracture within the weld zone for certain factor combinations. The significance of process factor levels on microstructure, fracture characteristics, and weld zone strength, inclusions, and embrittlement was analyzed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.