Abstract
Film coating thickness and terahertz electric field peak strength (TEFPS) were determined using terahertz pulsed imaging (TPI) and employed for the analysis of sustained-release coated pellets (theophylline layered sugar cores coated with Kollicoat ® SR:Kollicoat ® IR polymer blends). The effects of coating thickness, drug layer uniformity and optional curing were investigated using eight batches of pellets. Ten pellets from each batch were imaged with TPI to analyse the coating morphology (depicted in TEFPS) and thickness prior to release measurements. The results showed TEFPS values of 15.8% and 14.5% for pellets with a smooth drug layer coated at 8.2 and 12.5% (w/w) polymer weight-gain, respectively. Whereas 6.7% was derived for pellets with a coarse drug layer coated at both weight-gains. Although there were major differences in TEFPS, the resulting drug release kinetics were very similar. It was also shown that a 36 μm coating thickness difference was not drug release rate determining. These results suggested that drug release for the pellets studied was not predominately governed by drug diffusion through the polymeric film coating but probably to a large extent limited by drug solubility. TPI proved to be highly suitable to detect non-homogeneities in the drug layer and polymeric film coating.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.