Abstract

The effects of filler metal (FM) composition on inclusions and inclusion defects for ER NiCrFe-7 weldments have been investigated and analyzed. Results show that as Al, Ti content in FM increases from 0.14 wt% Al, 0.30 wt% Ti to 0.42 wt% Al, 0.92 wt% Ti, the Al, Ti reduction will increase during welding. Inclusion defects (point-like defects named by welding workers) are prone to form in the high Al, Ti content weldments. Inclusion defects with Mg, Ca, Al, and Ti as major metallic elements have been found on the surface and interior of the weldments, as Al, Ti content in FM is over 0.29 wt% Al, 0.62 wt% Ti. Less Ti content in FM cannot prevent ductility-dip-cracking (DDC) through producing enough intragranular precipitates and lessening intergranular M23C6 precipitates. Nb can be used to replace Ti to reduce the sensitivity of the DDC in the NiCrFe-7 alloy weldments.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.