Abstract
Unidirectional SiCf/SiC-matrix composites with a pyrocarbon interface were prepared by hot-pressing SiC nano-powder via a liquid phase of sintering additives under high temperature (1900 °C) and applied pressure (20 MPa). The SiC reinforcing fiber volume fraction of the composites varied from 0 to 78 vol% and was found to have significant effects on densification and mechanical properties, where changes in failure mode, proportional limit stress, ultimate strength, and elastic modulus were observed. The mechanical properties were significantly enhanced with an increase in the fiber volume fraction until a moderately high fiber content was obtained, after which the ultimate strength of the composite degraded. These observations were related to the open porosity within the fiber bundles. Further, fiber strength was affected by fiber damage caused by contact with the surrounding matrix due to poor densification of the SiC nano-powder.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.