Abstract
AbstractIn contrast to existing methods that add specific substances to poly(l‐lactic acid)/poly(d‐lactic acid) racemic blends to enhance stereocomplexation, in this study, a crosslinkable epoxy resin (EP) was introduced into a racemic blend. The results showed that, when the mass ratio of EP to racemic blend was 0.2:1 (EP:racemic blend = 0.2), regardless of the amount of diethylenetriamine (DETA) curing agent, homo‐crystals in the racemic blend were essentially inhibited. With a fixed EP content, a 0.05:1 DETA to EP mass ratio resulted in a homogeneous poly(l‐lactic acid)/poly(d‐lactic acid)/EP/DETA mixture. Uniformly dispersed EP network promoted the stereocomplexation of the racemic blend from the melt, but delayed the lamellar thickening of the stereocomplex crystals during heating. Thus, the constrained chain diffusion caused by the uniformly dispersed EP network was likely responsible for these contradictory results. Introducing uniformly dispersed network into poly(l‐lactic acid)/poly(d‐lactic acid) racemic blends is presumably a promising approach for gaining more insight into poly(lactic acid) stereocomplexation. © 2020 Society of Industrial Chemistry
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.