Effects of environment and heat treatment on an oxygen plasma-treated polyimide surface and its adhesion to a chromium overcoat

Abstract

—The effects of oxygen plasma treatment time, duration of storage, and heat treatment on the surface chemistry of and Cr adhesion to Dupont RC5878 and Kapton polyimides were investigated using X-ray photoelectron spectroscopy (XPS), and contact angle and peel strength measurements. The XPS results indicate that the initial stage of plasma treatment involves oxygen adsorption with insignificant modification of the surface chemistry. After 5 s of plasma treatment the surface chemistry is modified, as suggested by the changes in the carbonyl and partially oxidized carbon functional groups' contributions to the C(1s) line shape. These modifications resulted in an increase in the peel strength and a decrease in the contact angle of water. Over the first month of storage, the intensity of the carbonyl functional group peak decreased, while the contact angle increased and reached a steady-state value of 30° after 20 days of storage. These changes are mainly attributed to moisture absorption. Importantly, the met...