Abstract
The effects of electropulsing treatment on the precipitation behaviour of grain boundary carbides in GH3044 alloy were investigated. The results showed that the initial temperature of precipitation of M23C6 type carbides on grain boundary could be decreased by electropulsing treatment under the condition of high current density of 10.0kA/mm2 with a frequency of 5Hz and pulse width of 15s. The volume percentage of M23C6 type carbide was greatly increased to 274.60% comparing with that of the aging treatment at the same temperature. However, the precipitation of M23C6 type carbide was inhibited by electropulsing treatment under the condition of high frequency of 45Hz with the current density of 2kA/mm2 and pulse width of 15s. The volume percentage of M23C6 type carbide was decreased to 18.81% comparing with that of the aging treatment at the same temperature. It has been found that the diffusion of solute atom in the alloy can be promoted by the electric effect with the electropulsing. As a result, the thermodynamic condition and kinetics of the precipitation of M23C6 type carbide were changed, and both the initial and peak temperatures of precipitation were decreased.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.