Abstract
Li2CO3-doped lead-free Ba(Zr0.2Ti0.8)O3 (short as BZT20) ceramics were prepared by solid-state reaction method. The effect of dwell time (2–8 h) during sintering on the microstructure, dielectric properties and diffuse phase transition behavior of these samples is firstly investigated. All samples sintered at 1250 °C for different dwell time are of a pure perovskite phase. As the dwell time increased from 2 to 4, 6 and 8 h, the average grain size increased from ∼15 to ∼45 μm and decreased to ∼8 μm at 8 h dwell time. The samples sintered for 4 h showed enhanced dielectric property and lower diffusivity with em = 15,756 and γ = 1.65. Moreover, the peak temperature Tm corresponding to the maximum value of the dielectric constant em decreased slightly with the increase of dwell time, which may be attributed to the grain size effects on Li2CO3 doped BZT20 ceramics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.