Abstract
We report the preparation of polybenzoxazole (PBO) fiber from polyhydroxyamide (PHA) precursor fiber which is free from strong acid such as polyphosphoric acid. We prepared the PHA fibers with different spin-draw ratios (SDRs) using a wet-spinning method and the PBO fibers with an SDR of 3.5 (SDR-3.5 PBO fibers) were prepared by various heat-treatment temperatures, and investigated their morphology, crystalline structure, and mechanical properties. The simultaneous thermogravimetric analysis-mass spectrometry (STA-MS) and field-emission scanning electron microscopy (FE-SEM) results confirmed that the diameter of the SDR-3.5 PBO fiber was much smaller than that of the SDR-3.5 PHA fiber, due to the release of water during the thermal cyclization reaction which forms the PBO structure. The wide-angle Xray diffraction (WAXD) pattern of the SDR-3.5 PBO fiber heat-treated at 350 °C (SDR-3.5 PBO 350 fiber) showed two peaks, at 2θ=14.83 ° and 24.38 °, and the diffraction angles dropped with increasing heat-treatment temperature. In addition, the initial modulus and tensile strength of the SDR-3.5 PBO fiber heat-treated at 550 °C (SDR-3.5 PBO 550 fiber) were found to be 19.1 GPa and 449.2 MPa, which were much higher than those of the SDR-3.5 PHA fiber, 9.3 GPa and 227.0 MPa, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.