ZnO thin films were prepared by DC reactive magnetron sputtering at room temperature. Two of them were annealed with different modes under vacuum condition. One was annealed with constant temperature of 300°C ; the other was annealed with temperature rising step by step from room temperature to 300°C . By comparing the microstructure and optical properties of the as-grown and annealed samples, the effects of different annealing modes on ZnO films performances were revealed. The experiment results investigated that the sample annealed with constant temperature of 300°C has the high grain size and surface roughness. Both of the two annealing modes could release the intrinsic stresses to some degree. The optical band gap of the samples narrowed after annealing, and the two annealed samples have almost the same band gap. Strong green emissions are observed for all the samples, but the emission intensity decreased of the sample annealed with the temperature rising step by step compared with that of other samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.