Abstract
(La0.5Sr0.5)CoO3 (LSCO) thin films have been fabricated on silicon substrate by the pulsed laser deposition method. The effects of substrate temperature and post-annealing condition on the structural and electrical properties are investigated. The samples grown above 650°C are fully crystalline with perovskite structure. The film deposited at 700°C has columnar growth with electrical resistivity of about 1.99×10−3 Ω cm. The amorphous films grown at 500°C were post-annealed at different conditions. The sample post-annealed at 700°C and 10−4 Pa has similar microstructure with the sample in situ grown at 700°C and 25 Pa. However, the electrical resistivity of the post-annealed sample is one magnitude higher than that of the in situ grown sample because of the effect of oxygen vacancy. The temperature dependence of resistivity exhibits semiconductor-like character. It was found that post-annealing by rapid thermal process will result in film cracks due to the thermal stress. The results are referential for the applications of LSCO in microelectronic devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.