Indium tin oxide (ITO) films were sputtered on corning glass substrate. Oxygen admixture and sputtering deposition parameters were optimized to obtain the highest transparency as well as lowest resistivity. Structural, electrical and optical properties of the films were then examined. Increasing deposition rate and film thickness changed the crystallographic orientation from (222) to (400) and (440), as well as higher surface roughness. It was necessary to apply substrate heating during reposition to get films with better crystallinity. The lowest resistivity of 5.36 x 10-4 Ω•cm was obtained at 750 nm film thickness. The films’ resistivity was increased by addition of oxygen up to 2% in the argon sputtering gas. All films showed over 85% transmittance in the visible wavelength range, possible for applications in photovoltaic and display devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.