Abstract
The ferroelectricity of (Al1−xScx)N (x = 0–0.34) thin films with various thicknesses was investigated. (Al1−xScx)N films were prepared at 400 °C on (111)Pt/TiOx/SiO2/(001)Si substrates by the radio frequency dual-source reactive magnetron sputtering method using Al and Sc targets under pure N2 gas or a mixture of N2 and Ar gases. The film deposited under N2 gas showed larger remanent polarization than those under N2 + Ar mixture. Ferroelectricity was observed for films with x = 0.10–0.34 for about 140-nm-thick films deposited under N2 gas. The x = 0.22 films showed ferroelectricity down to 48 nm in thickness from the polarization–electric field curves and the positive-up-negative-down measurement. The ferroelectricity of the 9 nm-thick film also was ascertained from scanning nonlinear dielectric microscopy measurement. These results reveal that ferroelectric polarization can switch for films with much broader compositions and thicknesses than those in the previous study.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.