Abstract
The effects of the sintering duration and powder fraction (Ag-coated Cu/SnAgCu) on the microstructure and reliability of transient liquid phase sintered (TLPS) joints are investigated. The results show that two main intermetallic compounds (IMCs, Cu6Sn5 and Cu3Sn) formed in the joints. The Cu6Sn5 ratio generally decreased with increasing sintering time, Cu powder fraction, and thermal treatment. The void ratio of the high-Cu-fraction joints decreased and increased with increasing sintering and thermal stressing durations, respectively, whereas the low-Cu-fraction counterparts were stable. We also found that the shear strength increased with increasing thermal treatment time, which resulted from the transformation of Cu6Sn5 and Cu3Sn. Such findings could provide valuable information for optimizing the TLPS process and assuring the high reliability of electronic devices.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.