Abstract
Effects Cu and Ni additions on Au embrittlement of eutectic Sn–Pb solder interconnections during a solid-state aging treatment were evaluated using a ball shear testing method. The addition resulted in a formation of Au-containing ternary intermetallic compounds, either Au–Sn–Cu or Au–Sn–Ni phase, inside the solder matrix during aging treatment. The fracture energy of the solder interconnection containing 2.9 wt% Cu remained almost the same up to 200 h of aging treatment at 150 °C, demonstrating the possibility of suppressing the Au embrittlement by forming ternary intermetallic phases inside the solder matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.