Abstract
The durability of catalysts in the polymer-electrolyte membrane fuel cell (PEMFC) is identified as a critical limiting factor for wide commercialization of fuel cells. Even though much progress has been made in understanding the degradation mechanisms, the phenomena of Pt dissolution and agglomeration and their contributing factors are not fully understood. In the present investigation, the effects of crossover hydrogen on Pt degradation are studied using an accelerated stress test (AST). The end-of-test (EOT) membrane-electrode-assemblies (MEAs) were characterized by X-ray diffraction (XRD), scanning-electron microscopy (SEM), and energy-dispersive X-ray (EDX). The results provided mechanistic understanding of Pt dissolution and agglomeration: Pt growth and agglomeration were found to be less severe with more crossover hydrogen due likely to the chemical reduction of Pt oxides by crossover hydrogen and the subsequently decrease in the amount of Pt ions formed via the oxide pathway.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.