Abstract
AbstractCurrent durability design models for reinforced concrete structures in chloride‐contaminated environments do not consider the effects of cracks, which in practice are almost inevitable. Literature reports controversial results on corrosion propagation time of carbon steel (CS) in cracked concrete, while fewer information can be found on stainless steel (SS) rebar, which can be employed as additional protection strategy. In this experimental study, corrosion initiation and propagation of CS and SS rebar in uncracked and cracked concrete are presented. Prismatic specimens, reinforced with CS and 304L SS bars were subjected to a loading procedure to induce longitudinal micro‐cracks and exposed to a 3.5% NaCl solution for more than 2 years. Corrosion was monitored with electrochemical techniques and at the end of exposure corrosive attacks were observed. Results demonstrate the fundamental contribution of micro‐cracks in accelerating corrosion phenomena for CS, while SS is still in passive conditions also in cracked concrete.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.