Abstract
The effects of coupling agent, particle diameter (d), particle volume fraction (Vc), particle size distribution and average matrix ligament thickness (T̄) on the impact strength of high density polyethylene (HDPE)/CaCO3 composites have been investigated. A coupling agent is required for dispersing the CaCO3 particles (d∼0.6–5.6μm) without agglomeration in the HDPE matrix. The optimum weight ratio of coupling agent to CaCO3 particles for achieving the highest toughening efficiency is about 0.05, which is independent of d, Vc and size distribution of CaCO3 particles. HDPE/CaCO3 composites undergo a brittle–ductile transition in the range Vc=0.1–0.3, and the maximum impact strength achieved depends on d and size distribution. Above the transition, the impact strength of the composite decreases with increasing Vc. In general, a HDPE/CaCO3 composite with smaller d and broader size distribution has a higher toughness. A single brittle–ductile transition curve is not obtained when the impact strength is plotted against T̄. Shear yielding of the polymer matrix induced by debonding at the interface between CaCO3 and HDPE is shown to be the major toughening mechanism.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.