Abstract
With the addition of 0.075wt% graphene nanosheets (GNSs), the mechanical properties of coupled and aged solder joint were respectively investigated in this study. During the tensile tests, the weakening of the anode interface between intermetallic compounds (IMCs) and Bi layer significantly affected the ultimate tensile strength (UTS) of electromigration (EM) and thermal aging coupled solder joint. The formation of vacancies and stress concentration at the Cu–Sn–Zn/Cu–Zn interface in the aged solder joint was ascribed to the Bi segregation and GNSs. Nanoindentation results showed that the creep resistance of coupled solder joint was higher than that of the aged solder joint, which was because that the Bi layer, GNSs and cracks played a role of load transfer at the solder joint interface in coupled sample.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.