Effects of Copper and Austempering on Corrosion Behavior of Ductile Iron in 3.5 Pct Sodium Chloride

Abstract

Although alloying and heat treatments are common industrial practices to obtain ductile irons with desired mechanical properties, related information on how the two practices affect corrosion behavior is scarce. In this study, two ductile irons—with and without 1 wt pct copper addition—were austempered to obtain austempered ductile irons (ADIs). Polarization tests and salt spray tests were conducted to explore how both copper-alloying and austempering heat treatments influenced the corrosion behavior of ductile irons. The results showed that the corrosion resistance of 1 wt pct copper-alloyed ductile iron was better than that of the unalloyed one, while ADI had improved corrosion resistance compared with the as-cast. In particular, the ductile iron combined with the copper-alloying and austempering treatments increased the corrosion inhibition efficiency up to 84 pct as tested in 3.5 wt pct NaCl solution.