Abstract
Cu sheathed polycrystalline Ba0.6K0.4Fe2As2 superconducting wire was prepared by a two-step powder-in-tube method. A pressure of 2GPa was applied to a short sample before heat treatment. Magnetization and transport measurements were performed to investigate the effects of cold high pressure densification on the microstructure and superconductivity. The cold pressed sample shows an improved self-field transport critical current density of 2.8×104A/cm2 (Ic=83A) at 4.2K, which is nearly as twice as the unpressed sample. However, both samples manifest pronounced weak-link behavior, suggesting the technique need to be further optimized. The comparison of properties between pressed and unpressed sample and related mechanism was discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.