Abstract
Abstract Environmental barrier coatings (EBCs) are critical to the continued advancement of gas turbine hot section materials technology. EBCs are required to protect Si-based ceramics such as silicon carbide fiber-reinforced silicon carbide (SiC/SiC) ceramic matrix composites (CMCs) from oxidation and corrosion in the combustion environment. One of the current challenges concerning EBC lifetime is the thermochemical reactions between calcium-magnesium-aluminosilicate (CMAS) deposits and the EBC that leads to changes in both composition and stress state. These changes can severely reduce the integrity of the EBC leading to crack formation, delamination, and spallation. Current techniques for evaluating CMAS in the laboratory rely on the pre-application of CMAS. Two commonly used application methods to deposit CMAS on EBC materials are tape-cast and air spray. In both methods, the CMAS is applied to the EBC surface at ambient temperature, and then subjected to a heat treatment process for binder burnout. The purpose of this study is to compare the tape-cast and air spray methods on the CMAS corrosion of a ytterbium disilicate (Yb2Si2O7) EBC exposed to isothermal, and gradient thermal cycling. The results highlight if any differences exist in the CMAS infiltration kinetics between the two application methods.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.