Abstract
ABSTRACTThin films of colossal magnetoresistance material La0.7Ca0.3MnO3 were implanted with different fluence 200keV Cr ions. Resistivity measurements in zero and applied fields of up to 8T were made in order to determine the effects of the implanted magnetic ions on the magnetoresistance (MR). As the Cr fluence was increased, the resistivity increased and the metal-insulator transition (MI) temperature was suppressed to values below the experimentally accessible temperature range as a result of oxygen loss and the creation of defects. However, for the highest fluence of 5×1015 ions/cm2, a re-entrant metal-insulator type transition was observed. Furthermore a significant improvement in the low field MR was observed for fields less than 500mT. These results are interpreted in terms of substitution of Cr ions onto Mn sites and the creation of a magnetically inhomogeneous material and the influence of oxygen deficiency.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.