Ce addition to a hyperduplex stainless steel increased its resistance to pitting corrosion because of the formation of stable Ce oxides and a decrease in the area of microcrevices between the matrix and inclusions that act as pit initiation sites. In addition, Cr-enriched zones were formed around Ce oxides with low Cr content in the Ce added alloy. Pitting corrosion in the base alloy initiated at the microcrevice and propagated to Cr oxides, which deteriorated the pitting corrosion resistance. However, pitting corrosion in the Ce added alloy propagated not to the stable Ce oxides but to the matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.