Effects of ceramic thickness, ceramic translucency, and light transmission on light-cured bulk-fill resin composites as luting cement of lithium disilicate based-ceramics.

Abstract

To assess the effects of ceramic thickness, ceramic translucency, and light transmission on restorative composites used as luting cement for lithium disilicate-based ceramics. Four luting types of cement were tested (n=8); a dual-cured resin cement (Multilink N), a light-cured conventional flowable composite (Tetric N-Flow), and two light-cured bulk-fill flowable composites (Tetric N-Flow Bulk Fill and X-tra base). The 20 s- or 40 s-light (1000 mW/cm2) was transmitted through 1- or 2-mm-thick high- or low-translucency (HT- or LT-) ceramic discs (IPS e.Max press) to reach the 1-mm-thick luting cement. Light transmitted to cement without ceramic served as a control. Vickers hardness number (VHN), flexural strength (FS), fractography, and degree of conversion (DC) were evaluated. One-way and multi-way analysis of variance was conducted to determine the effects of factors on VHN and FS. Ceramic thickness, light transmission time, and cement type significantly affected the VHN of the luting cement (P < .000). Only Multilink N (LT- and HT-1mm) and Tetric N-Flow (HT-1mm) reached 90% VHN of corresponding control by 20 s-light transmissions, but Tetric N-Flow exhibited lowest VHN and approximately 1/3-1/2 VHN of Multilink N (P < 0.05). X-tra base expressed superior physicochemical properties to Tetric N-Flow Bulk Fill (P < 0.05) and reached >90% VHN of control in all conditions with 40 s-light transmissions except for LT-2 mm. DC, FS, and fractography supported these findings. The light-cured bulk-fill composite served as a luting cement for lithium-disilicate-based ceramics in a product-dependent manner. Light transmission time is crucial to ensure sufficient luting cement polymerization.