Abstract
The effects of Br− and I− concentrations on the cell voltage, anodic polarization, current efficiency (CE), and energy consumption (EC) of zinc electrodeposition from ammoniacal ammonium chloride solutions were investigated. The surface morphology of zinc deposits was also examined. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) were used to characterize the morphology of zinc deposits and the phase of anodic sediments produced during electrolysis. The results clearly showed that the CE slightly increased from approximately 95.12% in the absence of I− and Br− to 97.08% in the presence of 10 g·L−1 Br−; in contrast, the CE significantly decreased to less than 83% in the presence of 10 g·L−1 I−. The addition of Br− and I− positively affected the EC, which decreased from 2514 kW·h·t−1 to approximately 2300 kW·h·t−1. The results of anodic polarization measurements showed that the voltage drops were 130 and 510 mV when the concentrations of Br− and I− were 10 g·L−1 at a current density of 400 A·m−2, respectively. SEM images showed that the addition of Br− and I− caused different crystal growth mechanisms, which resulted in the production of compact and smooth zinc deposits. The anodic reactions of I− were also studied.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Minerals, Metallurgy, and Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.