Abstract
The effects of borax (sodium borate) on the enhancement reduction of pre-oxidized Panzhihua ilmenite were investigated. The effects of borax on the mineral phase transformation, microstructures, crystal cell parameter, melting point and Mg distribution were studied to reveal the mechanism of enhancement reduction. Under the constant reduction conditions, the borax could reduce the reduction activation energy of pre-oxidized ilmenite. The reduction kinetics analysis indicated that the reduction rate was controlled by interfacial chemical reaction. The reduction activation energy of the pre-oxidized ilmenite with 4% borax was 80.263 kJ/mol, which was 28.585 kJ/mol less than that of the pre-oxidized ilmenite without borax. Borax could eliminate the migration of Mg into the reduced particle center. The crystal cell parameter of the reduced product was increased by adding borax. Borax could improve the growth of dendritic crystals in the pre-oxidized ilmenite.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.