Abstract
Aluminum nitride (AIN) ceramics, with binary additives B2O3-Y2O3, were sintered at temperatures from 1700 to 1850 °C. The microstructure and sintering characteristics were studied by XRD, HREM, SEM and TEM/EDS, which showed that Y2O3 gave different yttrium aluminates through the reaction with Al2O3 under different conditions. With the increase of sintering temperature, the yttrium-to-aluminum atomic ratio Y/Al decreased in the secondary phases of the sintered bodies. It was discovered that B2O3 could dissolve in the yttrium aluminates, forming some ordered structure with a superlattice. After sintering at 1850 °C for 4 h, a specimen with a fine microstructure and a thermal conductivity of 190 W m−1 K−1 was obtained.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.