Effects of ballooning and rupture on the fracture resistance of Zircaloy-4 fuel cladding tube after LOCA-simulated experiments

Abstract

To investigate the relationship between the fracture resistance of a cladding tube and the amount of deformation of the cladding tube due to ballooning and rupture during a loss-of-coolant accident (LOCA), four-point-bending tests were performed using non-irradiated Zircaloy-4 cladding tubes which experienced a LOCA-simulated sequence (ballooning, rupture, high temperature oxidation and quench). According to the obtained results, it was found that the maximum bending stress of the cladding tube after the LOCA-simulated sequence, which was defined as the fracture resistance, correlated to the average thickness of prior-β layer in the cladding tube. Based on the average thickness of prior-β layer, the fracture resistance of the cladding tube with ballooning and rupture was expressed as functions of isothermal oxidation time and temperature and the maximum circumferential strain on the cladding tube.